PVC Compound for Cable CAS NO.9002-86-2
- Min.Order: 100 Kilogram
- Payment Terms: T/T,
- Product Details
Keywords
- PVC Cable injection & extrusion molding
- POLY(VINYL CHLORIDE) profiles,pipes fittings
- pvc blue CAS 9002-86-2
Quick Details
- ProName: PVC Compound for Cable
- CasNo: 9002-86-2
- Molecular Formula: [C2H3Cl]n
- Appearance: Granule
- Application: pvc profiles,pipes fittings, and many ...
- DeliveryTime: 7-20 days according to the quantities ...
- PackAge: Poly Bag Standard Package: 25 kg/bag. ...
- Port: Tianjin
- ProductionCapacity: 100000 Metric Ton/Day
- Purity: 100%
- Storage: Ordinary
- Transportation: By Sea and By Air
- LimitNum: 100 Kilogram
- Solid Content: 100%
Superiority
1.Shape:granules
2.color:according to your demand
3.processing method:extrusion molding
4.standard:3A.ISO9001:2008,14001,SGS,famous brand in China
5.feature:eco-friendly or not,non-peuliar smell,cold-esistant,bright colorful,high elongation at break,tensile strength
Details
Oval granules,3~4mm diameter, good plastication , the color and luster is even, smooth surface, no paste resin on surface.
|
Density (g/cm3) |
Hardness (shore A) |
Tensile Strength (Mpa) |
Elongation at break (%) |
Color |
|
1.26 |
82 |
21.83 |
372.96 |
Transparent |
|
1.32 |
83 |
16.42 |
325.56 |
Colorful |
|
1.32 |
84 |
20.07 |
330 |
Black |
|
1.46 |
94 |
16.4 |
254 |
Yellow |
|
1.51 |
82 |
11 |
310 |
Colorful |
|
1.59 |
67 |
8 |
256 |
Colorful |
|
1.61 |
75 |
10 |
330 |
Colorful |
|
VNC 3902HT |
|||
|
Applications |
High temperature insulation and sheathing grades - Lead based compound for wires and cables, (105℃ rating). Standards UL 758 |
||
|
Properties
|
Unit
|
Test method
|
Typical Values |
|
Density
|
g/cm3 |
ISO 1183 |
1.43 |
|
Hardness
|
Shore A,D |
ISO 868 |
88 |
|
Volume resistivity
|
Ohm.cm |
NFC 26-215 |
1.E + 14 |
|
Tensile strength
|
Mpa |
IEC 811 1:1 |
18 |
|
Elongation at break
|
% |
IEC 811 1:1 |
200 |
|
Variation of Tensile Strength after aging |
% |
7 days @ 80oC |
≤ 25 |
|
Variation of Elongation at break after aging |
% |
7 days @ 80oC |
≤ 35 |
|
Congo Red at 200°C |
Minute |
IEC 811 1:1 |
100 |
|
Oxygen Index % Min |
% |
ISO 4589 |
31 |
|
HCl Emission mg/g max |
|
IEC 754-1 |
NA |
|
Processing Suggestions |
The end users are advised to determine the optimum processing conditions by themselves. It varies with the types of extruder, speed of extrusion & thickness. As a guide, the typical barrel temperatures as follows: 150 (Z1), 155 (Z2), 155 (Z3), 160 (Z4), 165 (Head), 170 (Die) ℃ |
||